Zhermack Silicone XTX 45 - 5.5kg (5kg + 500g)

Zhermack Silicone XTX 45 – 5.5kg (5kg + 500g)

XTX 45 is a two-part, clear, pourable, addition-cure, room-temperature vulcanizing silicone suitable for rapid prototyping. The hardened rubber has a long service life and excellent long-term stability of the mechanical properties that guarantee the precision of the reproduction. Zhermack Silicone XTX 45 is suitable for industrial use.

applications

XTX 45 DRY is suitable for rapid prototyping (high transparency , high mechanical properties).

Important recommendations

• Before handling the product, read the safety data sheet and make sure you have all the information necessary for safe use.
• The platinum catalyst is included in the CATALYST component. CATALYST and BASE components may only be used together if they have the same lot number. The surfaces with which the material comes into contact must be perfectly clean, free of grease and dry.
• Test the product in small amounts before using it on a larger scale.
• Before use, homogenization of the two components is recommended to avoid deposits.
• The exact 10:1 ratio must be maintained to ensure the final properties of the product.
• Vaseline oil could do that vulcanization affect the product. Do a little test first.
• It is recommended a vacuum Use to remove any air bubbles.
• If necessary, use compressed air to facilitate this separation. Do not use tools to force the model to separate from the mold.
• The working and setting time decreases when the temperature exceeds 23°C (eg at a temperature of 40°C the working and setting time is approximately halved). If the temperature is below 23°C, the working and setting times will increase significantly.
• Cap the bottles after use.

More product information:
Colour: transparent
Density: 1.04 g/cc
Mixture: 10:1 (10 parts Base : 1 part Catalyst) by weight
viscosity :50000 mPas
Mixing time at 23 degrees Celsius: 1 min
processing time at 23 degrees Celsius: 60 minutes
Curing time at 23 degrees Celsius: 12 hours
hardness Shore A after 24 hours: 41
Breaking load 5.6 N/mm²
Elongation at break 380%
tear strength (Die B) 21N/mm